|Title:||Dielectric properties of complex structured (1-x)Pb(Zr<inf>0.52</inf>Ti<inf>0.48</inf>)O<inf>3</inf>- X(Bi<inf>3.25</inf>La<inf>0.75</inf>)Ti<inf>3</inf>O<inf>12</inf>ceramics|
|Keywords:||Materials Science;Physics and Astronomy|
|Abstract:||The ceramics with formula (1-x)PZT - xBLT were fabricated by a solid-state reaction method. X-ray diffractometry indicated complete solid solutions occurred for all compositions. Perovskite phase with tetragonal crystal structure and corresponding lattice distortion was observed. PZT-rich ceramics also possessed relatively high densities due to their more equiaxed grains with high packing capability compared to the ceramics with an addition of plate-shaped BLT. Measurement of dielectric constant indicated a gradual decrease with increasing BLT content. PZT ceramic exhibited a peak of phase transition, while broader peak were seen for PZT - BLT solid solutions, suggesting more diffuse transformation occurred due to an addition of BLT. A shift of transition temperature (Tc) to lower temperature was also observed in the PZT - BLT solid solutions. Copyright © Taylor & Francis Group, LLC.|
|Appears in Collections:||CMUL: Journal Articles|
Files in This Item:
There are no files associated with this item.
Items in CMUIR are protected by copyright, with all rights reserved, unless otherwise indicated.