Title: The mechanical and electrical properties of modified-BNKT lead-free ceramics
Authors: P. Jaita
S. Manotham
P. Butnoi
R. Sanjoom
P. Arkornsakul
D. R. Sweatman
C. Kruea-In
T. Tunkasiri
Keywords: Engineering
Materials Science
Physics and Astronomy
Issue Date: 12-Feb-2018
Abstract: © 2018, Copyright © Taylor & Francis Group, LLC. This research was conducted to study influence of ferric oxide nanoparticles on the properties of modified BNKT ceramics. The optimum sintering temperature was 1125°C at which all compositions had low porosity (0.12–0.19%). Raman and XRD showed coexisting rhombohedral and tetragonal phases throughout the entire compositional range. The Pr, d33and g33were slightly degraded when the additive was added. The maximum room temperature dielectric (ϵ′ = 1689, tan δ = 0.0606) and mechanical properties (HV = 5.6 GPa, HK = 4.9 GPa, E = 93 GPa and KIC= 1.58 MPa.m1/2) was obtained for the 2 vol% sample.
URI: https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=85045003975&origin=inward
http://cmuir.cmu.ac.th/jspui/handle/6653943832/58689
ISSN: 16078489
10584587
Appears in Collections:CMUL: Journal Articles

Files in This Item:
There are no files associated with this item.


Items in CMUIR are protected by copyright, with all rights reserved, unless otherwise indicated.