Title: Dielectric, mechanical, and microstructural characterization of HA-BST composites
Authors: S. Inthong
T. Tunkasiri
G. Rujijanagul
K. Pengpat
C. Kruea-In
U. Intatha
S. Eitssayeam
Keywords: Chemical Engineering
Materials Science
Issue Date: 1-Jan-2015
Abstract: © 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved. Hydroxyapatite (HA) is an excellent inorganic biomaterial and has various applications because its structure is similar to the inorganic matrix of human bone and dental enamel. In this present study, the HA-(Ba<inf>0.7</inf>Sr<inf>0.3</inf>)TiO<inf>3</inf>; HA-BST composites were synthesized by a solid state reaction technique. The phase, densification, microstructure, mechanical and dielectric properties of HA-BST composites sintered at 1350 °C were investigated. The HA-BST composite showed an increase in densification, Vickers hardness, Young's modulus and fracture toughness with maximum value as 3.42 g/cm<sup>3</sup>, 5.01 GPa, 161.70 GPa, and 1.48 MPa m<sup>1/2</sup>, respectively. The average grain size was decreased from 12.09 μm for a reference HA sample to 1.14 μm for the 30 wt% BST in HA-BST composites. The dielectric constant as a function of temperature and frequency tend to increase with increasing BST contents.
URI: https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84937512713&origin=inward
http://cmuir.cmu.ac.th/jspui/handle/6653943832/54267
ISSN: 02728842
Appears in Collections:CMUL: Journal Articles

Files in This Item:
There are no files associated with this item.


Items in CMUIR are protected by copyright, with all rights reserved, unless otherwise indicated.