|Title:||Effects of Bi<inf>0.5</inf>Na<inf>0.5</inf>TiO<inf>3</inf> dopant on microstructure and thermoelectric properties of Na<inf>x</inf>CoO<inf>2</inf> ceramics|
|Keywords:||Chemical Engineering;Chemistry;Engineering;Materials Science;Physics and Astronomy|
|Abstract:||Copyright © 2015 American Scientific PublishersAll rights reserved. Bi0.5Na0.5TiO3-doped NaxCoO2 ceramics with varied doping concentration of 0, 0.01, 0.03, 0.05 and 0.07 mol fraction were prepared by conventional solid state reaction method. The firing condition used was 950 °C for 8 h. X-ray diffraction pattern results showed that all produced ceramics were single phase with a hexagonal structure. Due to the substitution of BNT inside NaxCoO2 lattice, there was a slight shift of X-ray diffraction pattern to the left which indicated the lattice expansion. The scanning electron micrographs of ceramics indicated that small amount of BNT addition could eliminate pore and improved densification. A small amount of undissolved BNT was also present in NaxCoO2 matrix and dispersed at grain boundaries causing a decrease in grain size of the ceramic. The electrical conductivity and Seebeck coefficient of ceramics showed that all samples possessed metallic conduction behavior. However, BNT addition caused a reduction of electrical conductivity, Seebeck coefficient and power factor of NaxCoO2 ceramics.|
|Appears in Collections:||CMUL: Journal Articles|
Files in This Item:
There are no files associated with this item.
Items in CMUIR are protected by copyright, with all rights reserved, unless otherwise indicated.