dc.description.abstractModified sol-gel method was used to synthesize high purity titanium dioxide (TiO2) nanoparticles. The TiO2nanoparticles were synthesized by hydrolysis and condensation of titanium tetraisopropoxide in absolute ethanol using cellophane membrane. The use of cellophane membrane offers the advantage of well-controlled diffusion rate. Phase transformation, crystallite size, and phase composition of the calcined TiO2nanoparticles were derived from X-ray diffraction analysis by fundamental approach and the Rietveld method. The Brunauer, Emmett and Teller (BET) adsorption-desorption of nitrogen gas for specific surface area determination at the temperature of liquid nitrogen was performed on TiO2samples. The sample of pure anatase calcined at 400 °C for 3 h possessed high specific surface area of 121 m2/g. The particles morphology of the samples was examined by transmission electron microscopy (TEM). The crystallite sizes of anatase phase increased from 15 nm at 400 °C to 60 nm at 700 °C. The photocatalytic activities of TiO2nanoparticles were investigated with oxalic acid, formic acid, and malonic acid. Under near-UV irradiation, it was found that TiO2nanoparticles calcined at 400 °C for 3 h showed the highest activity for mineralizing oxalic acid. © 2007 Elsevier B.V. All rights reserved.en_US
dc.subjectMaterials Scienceen_US
dc.subjectPhysics and Astronomyen_US
dc.titleEffect of temperature on the degree of anatase-rutile transformation in titanium dioxide nanoparticles synthesized by the modified sol-gel methoden_US
article.title.sourcetitleCurrent Applied Physicsen_US
article.volume8en_US Mai Universityen_US
Appears in Collections:CMUL: Journal Articles

Files in This Item:
There are no files associated with this item.

Items in CMUIR are protected by copyright, with all rights reserved, unless otherwise indicated.