Title: Energy transfer from Gd<sup>3+</sup>to Sm<sup>3+</sup>and luminescence characteristics of CaO–Gd<inf>2</inf>O<inf>3</inf>–SiO<inf>2</inf>–B<inf>2</inf>O<inf>3</inf>scintillating glasses
Authors: N. Wantana
S. Kaewjaeng
S. Kothan
H. J. Kim
J. Kaewkhao
Keywords: Biochemistry, Genetics and Molecular Biology
Chemistry
Physics and Astronomy
Issue Date: 1-Jan-2017
Abstract: © 2016 Elsevier B.V. In this work, density, optical, photoluminescence and x-ray scintillation properties of calcium gadolinium silicoborate glass (CaO:Gd2O3:SiO2:B2O3) have been investigated. Glasses were prepared by the conventional melt quenching technique. The results show that the density of glass increased with increasing of Sm2O3. The optical spectra of glass shows eleven discrete absorption bands at 360, 373, 403, 475, 944, 1077, 1225, 1368, 1468, 1520 and 1586 nm which are due to the transitions of6H5/2to4D3/2,6P7/2,6P3/2,4I11/2,6F11/2,6F9/2,6F7/2,6F5/2,6F3/2,6H15/2and6F1/2, respectively. The emission spectra were observed and assigned to 312, 563, 600, 646 and 703 nm by excitation at 275 nm. The emission intensity of Sm3+increased with increasing of Sm2O3concentration until 0.25 mol%, while decay time decrease with increasing of Sm2O3content. For results of the radioluminescence (RL), they perform four emission peaks with the strongest emission at 598 nm. Glass doped with 0.35 mol% Sm2O3show the highest RL emission. The integral scintillation efficiency of 0.35 mol% Sm2O3doped glass was determined as 25% of commercial BGO scintillator crystal.
URI: https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84991290289&origin=inward
http://cmuir.cmu.ac.th/jspui/handle/6653943832/56843
ISSN: 00222313
Appears in Collections:CMUL: Journal Articles

Files in This Item:
There are no files associated with this item.


Items in CMUIR are protected by copyright, with all rights reserved, unless otherwise indicated.