Title: Effect of silver-loaded kaolinite on real ageing, hydrolytic degradation, and biodegradation of composite blown films based on poly(lactic acid) and poly(butylene adipate-co-terephthalate)
Authors: Sutinee Girdthep
Patnarin Worajittiphon
Thanawadee Leejarkpai
Robert Molloy
Winita Punyodom
Keywords: Chemistry
Materials Science
Physics and Astronomy
Issue Date: 1-Sep-2016
Abstract: © 2016 Elsevier Ltd Effect of silver-loaded kaolinite (AgKT) on real ageing, hydrolytic degradation inclusive of biodegradation of blown films of partially compatibilized poly(lactic acid) (PLA)/poly(butylene adipate-co-terephthalate) blend was investigated. Neat PLA showed the highest degradation extent, followed by the blend and the composite, respectively. The AgKT in the composite films induced crystallization, during film fabrication and hydrolysis, and acted as barrier to water adsorption, thus retarding polymer degradations. The composite film maintained its mechanical properties over a six-month ageing period with tensile strength and elongation at break as high as about 32 MPa and 140%, respectively, in transverse direction. The composite showed its biodegradation extent of 69.94% (after 90 days), conforming to the Chinese National Standard (GB/T 20197-2006) and thus offering good biodegradability for use as a material for the production of degradable plastic bags. This article demonstrated that the ageing, hydrolytic degradation, and biodegradation of PLA-based films could be tailored by AgKT incorporation. Our hypothesis on degradation phenomena at the molecular level was also suggested. Moreover, this composite formulation could be used for high-performance packaging with good biodegradability conformity.
URI: https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84980350793&origin=inward
http://cmuir.cmu.ac.th/jspui/handle/6653943832/55441
ISSN: 00143057
Appears in Collections:CMUL: Journal Articles

Files in This Item:
There are no files associated with this item.


Items in CMUIR are protected by copyright, with all rights reserved, unless otherwise indicated.