Please use this identifier to cite or link to this item: http://cmuir.cmu.ac.th/jspui/handle/6653943832/54482
Title: Effect of Er<inf>2</inf>O<inf>3</inf>dopant on electrical and optical properties of potassium sodium niobate silicate glass-ceramics
Authors: Ploypailin Yongsiri
Somnuk Sirisoonthorn
Kamonpan Pengpat
Keywords: Engineering
Materials Science
Physics and Astronomy
Issue Date: 1-Sep-2015
Abstract: © 2015 Elsevier Ltd. All rights reserved. In this study, transparent glass-ceramics from potassium sodium niobate (KNN)-silicate glass system doped with erbium oxide (Er2O3) were successfully prepared by incorporation method. KNN was added in glass batches as heterogeneous nucleating agent. The KNN powder was mixed with SiO2and Er2O3dopant with KNN and Er2O3content varied between 70-80 and 0.5-1.0 mol%, respectively. Each batch was subsequently melted at 1300°C for 15 min in a platinum crucible using an electric furnace. The quenched glasses were then subjected to heat treatment at various temperatures for 4 h. XRD results showed that the prepared glass ceramics contained crystals of KNN solid solution. In contrary, dielectric constant (εr) and dielectric loss (tan δ) were found to increase with increasing heat treatment temperature. Additionally, optical properties such as absorbance and energy band gap have been investigated.
URI: https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84939936730&origin=inward
http://cmuir.cmu.ac.th/jspui/handle/6653943832/54482
ISSN: 00255408
Appears in Collections:CMUL: Journal Articles