Title: Enhancement in dielectric, ferroelectric, and electrostrictive properties of Pb(Mg<inf>1/3</inf>Nb<inf>2/3</inf>)<inf>0.9</inf>Ti<inf>0.1</inf>O<inf>3</inf>ceramics by CuO addition
Authors: M. Promsawat
J. Y.Y. Wong
Z. Ren
H. N. Tailor
A. Watcharapasorn
Z. G. Ye
S. Jiansirisomboon
Keywords: Engineering
Materials Science
Issue Date: 1-Jan-2014
Abstract: Effects of CuO on dielectric, ferroelectric and electrostrictive properties of Pb(Mg1/3Nb2/3)0.9Ti0.1O3(PMNT) ceramics were studied. The PMNT/xCuO (with x = 0, 0.2, 0.4, 2.0 and 4.0 mol.%) ceramics were prepared by using solid state reaction and sintering process. It was found that the pseudo-cubic lattice parameter, a, gradually increased while the angle α decreased with increasing CuO content. Maximum dielectric constant showed a decreasing trend with increasing CuO with an abrupt increase in value at x = 2.0 mol.%. The temperature of maximum dielectric constant and depolarization temperature tended to increase while the diffuseness of dielectric peak decreased with increasing CuO concentration. Remanent polarization and coercive field of pure PMNT sample were ∼1.8 μC/cm2and 0.6 kV/cm, respectively, which were increased to ∼3.5 μC/cm2and 1.8 kV/cm when x = 0.2 mol.%. With x > 0.2 mol.%, coercive field gradually decreased with increasing CuO content while remanent polarization did not significantly change. With x ≤ 2.0 mol.%, induced strain and electrostrictive coefficient tended to increase with increasing CuO content, with maximum values of 0.09% (at 10 kV/cm) and 19.90 × 10-16m2/V2, respectively, for the PMNT/2.0 mol.% CuO sample. An enhancement in polar order of PMNT ceramics due to an addition of CuO was observed. © 2013 Elsevier B.V. All rights reserved.
URI: https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84888249265&origin=inward
http://cmuir.cmu.ac.th/jspui/handle/6653943832/53565
ISSN: 09258388
Appears in Collections:CMUL: Journal Articles

Files in This Item:
There are no files associated with this item.


Items in CMUIR are protected by copyright, with all rights reserved, unless otherwise indicated.