Title: Microstructural, physical, and thermal analyses of Portland cement-fly ash-calcium hydroxide blended pastes
Authors: T. Nochaiya
W. Wongkeo
K. Pimraksa
A. Chaipanich
Keywords: Chemistry
Physics and Astronomy
Issue Date: 1-Apr-2010
Abstract: The effect of calcium hydroxide (CH) on the properties of Portland-fly ash cement pastes, at up to high-volume fly ash mixes has been investigated using normal consistency, setting time, compressive strength, thermal analysis and scanning electron microscope. CH as an additive material (5 and 10 wt%), lignite fly ash (FA) up to 50 wt% was used to produce Portland cement (PC)-FA-CH pastes at w/PC + FA ratio of 0.5. Water requirement for normal consistency was found to increase with increasing CH content while a decrease in initial setting time was found. Furthermore, the compressive strengths of all FA mixes with CH were found to be higher than the mixes without CH. Thermal analysis and scanning electron microscope were used to study the hydration of PC-FA-CH system. The results showed that the first phase transition detected by thermal analyses was attributed to ettringite, calcium silicate hydrate, gehlenite hydrate and was found to be higher in PC-FA-CH mixes than in pure Portland-FA cement paste resulting in an increase in compressive strength. Moreover, the hydration phases were also found to increase with increasing curing time. Overall, the results show that the additional of 5 wt% CH in Portland-FA mixes especially at high-volume FA mixes was found to accelerate FA pozzolanic reaction at early ages (7 and 28 days), resulting to an increase in compressive strength. © 2009 Akadémiai Kiadó, Budapest, Hungary.
URI: https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=77951252169&origin=inward
http://cmuir.cmu.ac.th/jspui/handle/6653943832/50678
ISSN: 13886150
Appears in Collections:CMUL: Journal Articles

Files in This Item:
There are no files associated with this item.


Items in CMUIR are protected by copyright, with all rights reserved, unless otherwise indicated.